Float glass
Contents |
[edit] Introduction
Float glass (sometimes referred to as clear float glass) is glass that that has been manufactured from molten glass floated on the surface of a heated liquid of greater density such as tin (or in the past, lead) and then cooled. The result is a smooth glass of uniform thickness that gives undistorted vision, high light transmission and optical clarity.
Float glass is the most widely used form of glass for consumer applications. While in a semi-molten, waxy state, it can be easily shaped and formed to suit a variety of uses. Once made, it can be further processed to create other types of specialist glass, such as toughened glass, laminated glass and acoustic glass.
[edit] Manufacture
The first commercial application of the float glass process (the ‘Pilkington process’) of forming a continuous ribbon of glass floated on a molten tin surface was devised in the mid-1950s by Sir Alastair Pilkington and Kenneth Bickerstaff at Pilkington Brothers in the UK. The glass was flattened by its self-weight and flowed through the process under the influence of gravity. However, it was not until 1960 that the bulk process was made a commercial success.
The raw materials that go into float glass mainly include silica sand, soda ash, limestone and other ingredients. Once mixed, the materials are fed into a furnace with any recycled glass that may be included and heated to as high as 1,500°C to become a molten mass. It is then cooled before being poured into a tin bath.
Smoothness on the metal side is imparted by contact with the molten tin and on the upper surface (the air side) by polishing with fire. No additional polishing is required. Poured onto the molten tin in ribbons at an initial temperature of around 1,200°C, the speed of the glass through the process can be left to gravity or by top roller gears on the glass surface propelling it forward.
At around 1,100°C, the glass enters a lehr oven to be annealed i.e allowed to cool very gradually. This controlled cooling allows any internal stresses in the glass to dissipate. When it emerges from the oven, the glass is further cooled by jets of air after which scanners seek any imperfections which, if found, will result in the glass being discarded or recycled. Once at room temperature, the glass is trimmed and cut to suit customer requirements, after which the sheets are packed for shipping.
[edit] Applications
Because it results in a perfectly flat surface, float glass can be used in most flat-glass applications. It is available in a wide range of sizes and thicknesses for use in mirrors, automobile applications, windows, doors, insulated glass, light fittings and so on.
[edit] Related articles on Designing Buildings
Featured articles and news
Net zero electricity grids BSRIA guide NZG 5/2024
Outlining the changes needed to transition to net zero.
CIOB Global Student Challenge 2024
Universitas Indonesia wins for second year running.
New project and cultural district described in detail.
The nature of EPCs, crticism and inaccuracies.
History, issues and redesign.
From waste recycling to energy performance the hierchy.
An introduction to WERCS and WEEE responsibilities
Dealing 2 million tonnes of waste equipment a year.
Global BACS Market: analytics and optimisation
A BSRIA glance at building automation and control systems.
What it is and how to use it.
Types of insulating plaster by binder and insulant.
Investors in People: CIOB achieves gold
Reflecting a commitment to employees and members.
Scratching beneath the surface; a guide to selection.
ECA 2024 Apprentice of the Year Award
Entries open for submission until May 31.
UK gov apprenticeship funding from April 2024
Brief summary the policy paper updated in March.
For the World Autism Awareness Month of April.