The term ‘architectural fabrics’ generally refers to structural fabrics used to form tensile surfaces, such as canopies, roofs and other forms of shelter. Architectural fabrics are generally held in position by tension forces imposed by a structural framework, a cabling system, internal air pressure or a combination.
Typically, the membrane is formed by a fabric, consisting of a woven base cloth, coated on both sides with an impermeable polymer, and sometimes a durable topcoat, however a wide range of variations are available, ranging from open weave fabrics, to transparent foils.
Architectural fabrics are generally very thin, approximately 1mm thick and have very little compressive strength, but very high tensile strength.
The typical tensile strengths of architectural fabrics are set out below:
- Type 1: 3,000 N/5cm.
- Type 2: 4,000 N/5cm.
- Type 3: 5,550 N/5cm.
- Type 4: 7,000 N/5cm.
- Type 5: 9,000 N/5cm.
Cotton was one of the earliest materials used as an architectural fabric, and is still in use today. It is relatively inexpensive and is available in a wide range of colours, but it has a lower tensile strength than some more modern materials, and is prone to staining and shrinkage. It has a relatively short life expectancy, but can flex repeatedly without cracking, and so tends to be used for small-scale, temporary structures.
PVC coated polyester is the most commonly used architectural fabric. It is relatively inexpensive, has reasonable structural strength and translucency, can be joined relatively easily at seams by welding, and has an reasonable life expectancy.
Structurally, PVC polyester can last in excess of 20 years, however, it becomes more difficult to clean as the plasticisers used to make the PVC flexible leach to the surface, and so it is generally expected to last 10 to 15 years.
It is often manufactured with a topcoat such as PVDF (polyvinylidene fluoride), which improves its cleanability, but generally reduces its weldability, and so must be removed in the region of welded seams. Topcoats can increase the lifespan of PVC polyester to 15 to 20 years.
NB: PVC has been criticised for its environmental performance, with claims that the chemicals used to plasticise the PVC can be harmful to the environment. However, alternatives such as polyolefin coated polyester have struggled with fire resistance issues, and fire retardants added to the coating have resulted in reduced adhesion at seams.
PTFE (polytetrafluoroethylene or ‘Teflon’) coated glass can be stronger than PVC polyester, and is longer lasting, with a life in excess of 30 years. However, it is more expensive and is relatively inelastic, and so requires more accurate patterning.
PTFE is a cream colour when new, but bleaches white in sunlight and is generally self cleaning if regularly exposed to sunlight.
Whereas PTFE is translucent, silicone is transparent, and silicone coated glass has an anticipated life of up to 50 years. It has good fire resistance and low toxicity, but is not weldable, and so the seaming process requires an adhesive, and silicone can be difficult to keep clean.
 EFTE foil
Ethylene tetrafluoroethylene (ETFE) is a relatively transparent foil that can be used as a lightweight alternative to glass. It can be used as a single layer, or in multiple layers of up to 5 layers, inflated to form large cushions.
Other materials that have been used, sometimes only for experimental purposes, or in forms that were discontinued include:
 Uncoated fabrics
- Woven PTFE fibre (hydrophobic, microporous, durable and with approximately 40% light transmittance).
- High-density polyethylene (HDPE is not waterproof and is seamed by sewing).
 Mesh reinforced films
- Polyester reinforced PVC.
- Glass reinforced FEP.
- Aramid reinforced FEP.
- Steel reinforced FEP.
- Glass reinforced ETFE.
- Aramid reinforced ETFE.
- Steel reinforced ETFE
- Polyester reinforced ETFE.
- Glass reinforced PTFE.
 Coated fabrics
- Acrylic painted cotton.
- Vinyl coated cotton.
- High Silica Fabrics.
- Hypalon coated polyester.
- Neoprene coated nylon.
- Hypalon coated nylon.
- Polyolefin coated polyester.
- Polyester coated cotton.
- PTFE coated polypropylene.
- PTFE coated polyester.
- PTFE coated acrylic.
- ETFE coated glass.
- ETFE coated polyester.
- PVF coated glass.
- PTFE coated aramid.
- PVC coated aramid.
- PVDF coated polyester.
- PVDF coated glass.
- Vermiculite coated glass.
- Vinyl coated nylon.
- Vinyl coated polyester.
- Vinyl laminated polyester.
- Acrylic coated polyester.
- Polyurethane coated nylon.
 Multilayer and enhanced membranes
- Double layer fabrics.
- Triple layer fabrics.
- Inflated cushions.
- Active membranes.
- Insulated fabrics.
- Phase change fabrics.
 Related articles on Designing Buildings Wiki
- Buckminster Fuller.
- Fabric structures.
- Frei Otto.
- Glass reinforced concrete.
- Millennium Dome.
- Phase change materials.
- Polyvinyl chloride PVC.
- Ted Happold.
- The development of structural membranes.
- The history of fabric structures.
- The structural behaviour of architectural fabric structures.
- The thermal behaviour of spaces enclosed by fabric membranes.
Featured articles and news
Timber is a natural carbon sink, but it must not end up in landfill at the end of its useful life.
BSRIA has collaborated with the Department of Health on research into air permeability in isolation rooms.
New step-by-step route maps for implementing effective surface water management measures are published.
GMP is an agreement with a contractor that the contract sum will not exceed a specified maximum. Read more here.
The BREEAM Sustainability Champion is changing to the Advisory Professional - here's what you need to know.
A fresh round of job-cuts takes the total number of redundancies to over 1,000.
Read our introductory article to the completion date in construction contracts.
Almost 90% of freight in London is moved by road. The River Thames could add much needed extra capacity.
National Infrastructure Commission warn that large infrastructure projects are at risk of falling behind.
The quality of Cambridge owes as much to its open spaces as to its architectural uniqueness.